陈韶辉,郭峰,汪文睿,李传峰,杨爱武

• 1:中国石化扬子石油化工有限公司南京研究院

摘要(Abstract)：

通过对IVB族金属催化剂和稀土催化剂这两类茂金属催化剂的评述,介绍了催化剂结构与共聚性能,以及与由此得到的共聚物性能之间的关系,并指出了该领域茂金属催化剂研究的发展方向。

关键词(KeyWords)： 乙烯;降冰片烯;共聚;茂金属催化剂;进展

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 陈韶辉,郭峰,汪文睿,李传峰,杨爱武

参考文献(References)：

• [1]姚臻,吕飞,曹堃.环烯烃共聚物的制备[J].现代化工,2006,26(3):67-73.
• [2]姚臻,戴斌斌,刘少杰,等.乙烯和降冰片烯加成共聚合催化体系[J].化学进展,2010,22(10):2024-2032.
• [3]郑治明编译.环烯烃共聚物在聚烯烃复合膜中的应用[J].国外塑料,2011,29(11):46-47.
• [4]Randy Jester.COC增强聚烯烃包装薄膜的性能[J].现代塑料,2011,12:49-51.
• [5]马天,孔德鹏,姬江军,等.环烯烃共聚物多孔太赫兹纤维的设计与特性模拟[J].红外与激光工程,2013,42(3):631-636.
• [6]Wei Wang,Tatsuo Yanaka,Miki Tsubota,et al.Effect of cyclopentadienyl fragment in copolymerization of ethylene with cyclic olefins catalyzed by non-bridged(aryloxo)(cyclopentadienyl)titanium(IV)complexes[J].Advanced Synthesis and Catalysis,2005,347:433-446.
• [7]Kotohito Nomura,Hiroya Fukuda,Shohei Katao,et al.Olefin polymerization by half-titanocenes containingη2-pyrazolato ligands-MAO catalyst systems[J].Macromolecular,2011,44:1986-1998.
• [8]Xiaoyan Tang,Yongxia Wang,Baixiang Li et al.Highly efficient ethylene/norbornene copolymerization by o-di(phenyl)phosphanylphenolate-based half-titanocene complexes[J].Journal of Polymer science,part A:Polymer Chemistry,2013,51:1585-1594.
• [9]Kotohito Nomura,Wei Wang,Michiya Fujiki,et al.Notable norbornene(NBE)incorpotation in ethylene-NBE copolymerization catalysed by nonbridged half-titanocenes:better correlation between NBE incorpotation and coordination energy[J].Chemical Communications,2006,25:2659-2661.
• [10]Kotohito Nomura,Junji Yamada,Wei Wang,et al.Effect of ketimide ligand for ethylene polymerization catalyzed by(cyclopentadienyl)(ketimide)titanium complexes-MAO catalyst systems:Structural analysis for Cp*TiCl2(N=CPh2)[J].Journal of Organometallic Chemistry,2007,692:4675-4682.
• [11]Laura Boggioni,Giulia Scalcione,Andrea Ravasio,et al.Ethylene-co-norbornene copolymers grafted carbon nanotube composites by in situ polymerization[J].Macromolecular chemistry and physics,2012,213:627-634.
• [12]Wannida Apisuk,Alexandra G,Boonyarach Kitiyanan,et al.Efficient ethylene/norbornene copolymerization by halftitanocenes containing imidazolin-2-iminato ligands and MAO catalyst systems[J].Journal of Polymer science,part A:Polymer Chemistry,2013,51:2575-2580.
• [13]Kotohiro Nomura,Hiroya Fukuda,Wannida Apisuk,et al.Ethylene copolymerization by half-titanocenes containing imidazolin-2-iminato ligands–MAO catalyst systems[J].Journal of Molecular Catalysis A:Chemical,2012,363/364:501-511.
• [14]Walter kaminsky,Inken Beulich,Michael Amdt-Rosenau.Copolymerization of ethene with cyclic and other sterically hindered olefins[J].Macromolecular Symposium,2001,173:211-225.
• [15]Zhen Yao,Fei Lv,Shao Jie Liu,et al.Synthesis of ethylene and norbornene copolymer with metallocene catalysts and characteristic analysis[J].Journal of Applied Polymer Science.2008,107:286-291.
• [16]Shaojie Liu,Zhen Yao,Kun Cao.Comparison of thermal properties of ethylene-norbornenecopolymers prepared by batch and semi-batch processes[J].Journal of Applied Polymer Science.2009,112:2493-2496.
• [17]John Forsyth,Jose M Perena,Rosario Benavente,et al.Influence of the polymer microstructure on the thermal properties of cycloolefin copolymers with high norbornene contents[J].Macromolecular:Chemistry and Physics,2001,202:614-620.
• [18]Ralf Alexander Wendt,Gerhard Fink.Ethene-norbornene copolymerization using two different homogeneous metallocene catalyst systems and investigations of the copolymer microstructure[J].Journal of Molecular Catalysis A:chemical,2003,203:101-111.
• [19]Walter kaminsky,Phu-Dennis Tran,Ralf Werner.New polymers by copolymerization of ethylene and norbornene with metallocene catalysts[J].Macromolecular Symposium,2004,213:101-108.
• [20]Jianguo Ni,Chunsheng LV,Yuetao Zhang,et al.Norbornene polymerization and ethylene/norbornene copolymerization catalyzed by constrained geometry cyclopentadienyl-phenoxytitanium catalysts[J].Polymer,2008,49:211-216.
• [21]吕胜春,许云飞,颜子龙,等.乙烯与降冰片烯的共聚及产物表征[J].高分子材料科学与工程,2013,29(2):31-34.
• [22]Keun Byoung Yoon,Yeon Seok Choi,Seok Kyun Noh,et al.Ethylene/norbornene copolymerization with iPr(Cp)(Flu)ZrCl2catalyst:effect of MAO cocatalyst and 3rd monomer[J].Macromolecular Symposium,2004,260:27-33.
• [23]Tomoyuki Tada,Zhengguo Cai,Yuushou Nakayama,et al.Efficient molecular weight control with trialkylaluminum in ethylene-morbornene copolymerization by[Ph2C(Flu)(3-MeCp)]ZrCl2/methylaluminoxane catalyst[J].Macromolecular:Chemistry and Physics,2010,211:2132-2137.
• [24]Xiaofang Li,Jens Baldamus J,Zhaomin Hou.Alternating ethylene-norbornene copolymerization catalyzed by cationic half-sandwich scandium complexes[J].Angewandte Chemie International Edition,2005,44:962-965.
• [25]Andrea Ravasio,Cristina Zampa,Laura Boggioni et al.Copolymerization of ethylene with norbornene catalyzed by cationic rare-earth metal half-sandwich complexes[J].Macromolecules,2008,41:9565-9569.
• [26]Baoli Wang,Tao Tang,Yuesheng Li,et al.Copolymerization of ethylene with norbornene catalyzed by cationic rare earth metal fluorenyl functionalized N-heterocyclic carbene complexes[J].Dalton transactions:An international journal of inorganic chemistry,2009,41:8963-8969.櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬櫬毬毬毬毬最新专利文摘高流动性和增强力学性能的多相聚丙烯本发明涉及一种多相聚丙烯树脂,该树脂由一种结晶丙烯均聚物(A)和非结晶性丙烯共聚物相(B)组成,该多相聚丙烯树脂具有好的力学性能,特别在低温下流动性好。此外,本发明还涉及了一种多相聚丙烯树脂的生产工艺。USP9074085,2015-07-07可热封的多层聚丙烯树脂薄膜包装材料本发明涉及一种可热封的聚丙烯树脂多层薄膜,该膜具有良好的韧性和较高的热强度,所制作的包装袋适用于较重的物品包装,主要用于包装水果和蔬菜。这种包装薄膜是一种具有三层或更多层的复合薄膜,由结晶聚丙烯树脂作为基层,热封层熔点不超过150℃,还有一个中间层。复合薄膜的横向、纵向方向的弹性拉伸模量都为3.1~6.0GPa,密封时薄膜的热封能量不小于11N·cm(15mm宽的样品测试结果,下同),薄膜的热封强度不小于8 N。USP9085124,2015-07-21一种柔软聚丙烯电缆护套料本发明涉及一种柔软聚丙烯电缆护套料,包括以下质量份:聚丙烯树脂100份、柔性改性剂60~120份、润滑剂0.5~2份、抗氧剂0.5~1份、抗铜剂0.2~0.5份。该电缆护套料具有良好的耐低温性能和柔韧性能,可以有效改善聚丙烯电缆料原有的抗应力发白现象和其耐低温性。CN104744807A,2015-07-01高抗冲聚丙烯复合材料及其制备方法本发明提供了高抗冲聚丙烯复合材料及其制备方法,由聚丙烯树脂、超细碳酸钙填料和弹性体材料组成,包括以下质量份:聚丙烯树脂为100份、超细碳酸钙填料为14~30份、弹性体材料为7~15份。在保持聚丙烯材料的刚性不会明显降低的条件下能显著提升其耐冲击能力,从而实现改性后材料的刚性和韧性的平衡。CN104744806A,2015-07-01一种高韧性塑料本发明涉及一种高韧性塑料,由以下质量份组成:低密度聚乙烯7~19份、硬脂酸4~8份、增韧剂2~6份、改性有机溶剂3~7份、邻苯二甲酸二丁酯3~9份、聚苯乙烯树脂23~35份、偶联剂3~5份、淀粉12~36份、植物秸秆3~7份、马来酸酐1~3份、丙烯腈-丁二烯-苯乙烯共聚物6~11份、抗冲剂2~4份,。该高韧性塑料不仅生产工艺简单,还可以延长使用寿命。CN104817775A,2015-08-05一种高抗冲阻燃的塑料管材本发明公开了一种高抗冲阻燃的塑料管材。该管材具有遇火碳化面积小、无残焰、不阴燃等优点,阻燃性能达V2级,成型材料具有高强度、高抗弯性的特点,弯曲强度可达116 MPa,冲击强度可达6.5kJ/m2以上,拉伸强度可达42 MPa以上,应用前景广阔。CN104817764A,2015-08-05新型保险杠材料及其汽车保险杠本发明公开一种新型保险杠材料及其汽车保险杠,由以下质量份组成:聚丙烯35~55份、磷酸三氯乙酯2~10份、热塑性聚氨酯5~15份、顺丁橡胶3~10份、聚酰胺4`12份、乙丙橡胶3~11份、聚乙烯3~11份、剪切增稠液4~10份、聚间苯二甲酰间苯二胺纤维10~16份、抗静电剂1~6份、抗氧剂1~4份、分散剂4~10份、增塑剂1~5份、紫外线吸收剂1~5份。具有低收缩率、高流动、耐候性和油漆性能良好,同时具有高韧性、高强度、断裂伸长率高和热变形温度高的特点,汽车发生轻微碰撞时保险杠也不会出现破裂现象,相较于现有的保险杠材料,弯曲模量、拉伸强度、硬度和熔体流动速率均有大幅度提高,此外,在低温抗冲击性、耐化学品性上也有显著提高。CN104817769A,2015-08-05一种高硬度-高弹性-耐磨复合发泡材料及制备方法本发明提供了一种高硬度-高弹性-耐磨复合发泡材料及制备方法,属于高分子材料加工领域。由以下质量份组成:热塑性弹性体20~80份、乙烯-醋酸乙烯酯共聚物0~50份、聚乙烯0~30份、降黏剂5~30份、交联剂0.5~6份、发泡剂1~5份、发泡助剂2~6份、耐磨剂0.5~10份、填充剂10~30份、其它助剂1~4份。该材料不仅具有橡胶质感,而且具有高弹、耐磨、低压缩歪、耐折防皱等特点。可广泛应用于制造沙滩鞋、拖鞋、运动鞋等鞋材领域,还可应用于儿童拼图、泡沫地板,以及精密电子仪器、电器、医疗器械的包装材料。CN104817754A,2015-08-05塑料管的制备方法本发明公开一种塑料管的制备方法,属于塑料制品领域。包括以下步骤:先将聚丙烯和聚烯烃加热熔融,并搅拌均匀;向其中加入聚乙烯辛烯共弹性体、低铅复合稳定剂、钛白粉以及硬脂酸,搅拌均匀,然后再升温至160~165℃,保温反应3h;接着先降温至120~125℃,再向其中加入碳化硅,保温搅拌0.5h;放入模具中,挤压成型。本发明制得的塑料管具有良好的散热性能和拉伸性能。CN104817766A,2015-08-05一种改进聚乙烯锂电池隔膜表面活性的方法本发明公开了一种改进聚乙烯锂电池隔膜表面活性的方法。具体步骤:将改性聚烯烃材料溶解在白油中,得到含改性聚烯烃材料的白油混合物;将聚乙烯粉末与含改性聚烯烃的白油混合物一起喂入双螺杆挤出机,经计量、过滤、挤出模头和冷却装置得到含油铸片;含油铸片经双向拉伸得到含油隔膜;含油隔膜进入萃取槽中,利用萃取剂将含油隔膜中的白油萃取出来;采用热风或者热辊对萃取后的隔膜进行干燥;经横拉扩幅与热定型处理后得到成品隔膜。本发明通过掺杂部分带活性基团如羟基等基团的改性聚烯烃材料,使得基体材料表面具有一些可与涂覆材料发生化学结合的官能团,从而改善涂层与基体材料之间的结合力。CN104821382A,2015-08-05一种改善超高分子量聚乙烯耐磨性和强度的方法本发明涉及一种高性能超高分子量聚乙烯(UHMWPE)的制备方法。针对UHMWPE表面硬度低、抗磨损能力差、强度低及高温流动性能差等缺点,采用原子转移自由基聚合(ATRP)制备相容剂PE-b-M(M为硅烷偶联剂),将碳纳米管、二氧化硅、PE-b-M和超高分子量聚乙烯按一定比例加热混匀,使硅烷偶联剂和碳纳米管水解结合,得到性能优化的UHMWPE。改性的UHMWPE不仅相容性好,并且各项性能得到提高。CN104817751A,2015-08-05